(Elsevier Ltd., 2021) Karacasulu, Levent; Ögür, Ezgi; Pişkin, Cerem; Vakıfahmetoğlu, Çekdar; 03.09. Department of Materials Science and Engineering; 01. Izmir Institute of Technology; 01.01. Units Affiliated to the Rectorate; 03. Faculty of Engineering
Ordinary recycled soda lime glass powder was densified via cold sintering process with the aid of concentrated NaOH solution. Increase in processing time, temperature and concentration of the NaOH solution resulted in the formation of monolithic glass artifacts with higher relative densities. The sample densified the most (95.2%) was obtained when the sintering was performed at 250˚C with a 20 min dwell time using 15 M NaOH solution.