Title: | Photocatalytic and optical properties of zinc oxide structures prepared at different urea concentrations | Authors: | Uysal, Berk Şen, Selin Top, Ayben |
Keywords: | Zinc oxide Nanostructures Optical properties Photocatalyst N-doping |
Publisher: | Serban Solacolu Foundation | Abstract: | In this study, ZnO samples were synthesized using zinc acetate and urea with a method containing sonication, sol-gel transition and calcination steps. Urea to zinc acetate mole ratio values were changed as 0, 0.5, 1, and 2 and corresponding calcined samples were denoted as UZ-0, UZ-0.5, UZ-1, and UZ-2, respectively. Scanning electron microscopy (SEM) images indicated globular and rod-like structures. Aspect ratios of the nanorods increased as urea to zinc acetate ratio increased from 0 to 1 whereas nanoparticles with sizes of 70 +/- 20 nm were observed for UZ-2 sample. Brunauer, Emmett and Teller (BET) surface area values of the samples varied between 9 and 25 m(2)/g and increased as initial urea amount increased. Band gap energies of the samples ranged between 3.24 and 3.29 eV. Four major peaks at about 400, 420, 480 and 530 nm with different intensities were observed in the photoluminescence (PL) spectra of the samples. All the samples removed rhodamine B by both adsorption and photodegradation. The highest visible light induced photodegradation rate was exhibited by UZ-2 sample having the highest surface area and it is attributed to superior charge separation properties of this sample under visible light. | URI: | https://hdl.handle.net/11147/11774 | ISSN: | 1583-3186 |
Appears in Collections: | Chemical Engineering / Kimya Mühendisliği Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection |
Show full item record
CORE Recommender
SCOPUSTM
Citations
3
checked on Sep 1, 2024
WEB OF SCIENCETM
Citations
3
checked on Aug 24, 2024
Page view(s)
25,338
checked on Sep 2, 2024
Google ScholarTM
Check
Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.