Title: Effect of post fabrication aging treatment on the microstructure, crystallographic texture and elevated temperature mechanical properties of IN718 alloy fabricated by selective laser melting
Authors: Özer, Seren
Bilgin, Güney Mert
Davut, Kemal
Esen, Ziya
Dericioğlu, Arcan.F
Middle East Technical University
Middle East Technical University
Izmir Institute of Technology
Çankaya Üniversitesi
Middle East Technical University
Keywords: Additive manufacturing
Dynamic strain aging
Mechanical properties
Issue Date: Aug-2022
Publisher: Elsevier
Abstract: The effect of building direction and post fabrication aging treatment on the microstructure, crystallographic texture and high temperature mechanical properties of Inconel 718 (IN718) alloy fabricated by selective laser melting (SLM) method was investigated. After aging, arc-shaped structures seen in as-fabricated samples disappeared and converted into a mixture of columnar and equiaxed grains. Nano-sized γ″ and/or γ′ precipitates were formed upon aging; however, MC type carbides and Laves phase encountered in as-fabricated samples were not dissolved completely after aging. Moreover, aging did not alter the texture ((001)//building direction (BD)) of as-fabricated samples. Mechanical properties of the alloys under tension were influenced by the build direction, aging time and test temperature. As-fabricated samples produced in vertical direction exhibited higher room temperature strengths with lower ductility due to orientation of overlapped prior melt pools. Room temperature tensile test results revealed that peak aging caused a significant improvement in ultimate tensile strength (UTS), from 1066.5 MPa and 998.4 MPa to 1408.5 MPa and 1330.4 MPa whereas elongation values decreased from 27.5% and 32.2% to 19.6% and 23.7% in vertically and horizontally built samples, respectively. Peak-aged samples (aged at 700 °C for 8 h) tested at 600 °C displayed serrated regions in their stress-strain curves due to dynamic strain aging (DSA). Although strength values of the samples displayed an expected decrease by temperature, ductility of the samples reduced to minimum at temperatures around 700–800 °C, which was attributed to intermediate temperature embrittlement.
URI: https://doi.org/10.1016/j.jmatprotec.2022.117622
https://hdl.handle.net/11147/12097
Appears in Collections:Materials Science and Engineering / Malzeme Bilimi ve Mühendisliği
Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection

Files in This Item:
File Description SizeFormat 
1-s2.0-S0924013622001340-main.pdf
  Until 2025-07-01
Article18.74 MBAdobe PDFView/Open    Request a copy
Show full item record



CORE Recommender

SCOPUSTM   
Citations

11
checked on Mar 1, 2024

WEB OF SCIENCETM
Citations

9
checked on Mar 2, 2024

Page view(s)

12,586
checked on Feb 26, 2024

Google ScholarTM

Check




Altmetric


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.