Title: The strain rate sensitive flow stresses and constitutive equations of a selective-laser-melt and an annealed-rolled 316L stainless steel: A comparative study
Authors: Güden, Mustafa
Enser, Samed
Bayhan, Mesut
Taşdemirci, Alper
Yavaş, Hakan
Izmir Institute of Technology
Izmir Institute of Technology
Izmir Institute of Technology
Izmir Institute of Technology
Turkish Aerospace Industries
Keywords: Compressive flow stress
Flow stress equations
Strain rate sensitivity
Issue Date: 24-Mar-2022
Publisher: Elsevier
Abstract: The strain rate dependent compressive flow stresses of a Selective-Laser-Melt 316L (SLM-316L) alloy and a commercial (annealed-extruded) 316L (C-316L) alloy were determined, for comparison, between 1x10-4 and ∼2500 s-1 and between 1x10-4 and ∼2800 s-1, respectively. The Johnson and Cook flow stress material model parameters of both alloys were also determined. The microstructural examinations of the deformed cross-sections of tested specimens (interrupted tests) showed a twinning-induced-plasticity in SLM-316L alloy and a martensitic transformation-induced-plasticity in C-316L alloy. Twin and martensite formations were detected microscopically higher in the dynamically tested specimens until about 0.22 strain, while the twin and martensite formations decreased at increasing strains due to adiabatic heating. The rate sensitivity of SLM-316L was determined slightly higher than that of C-316L within the quasi-static strain rate range (1x10-4 and 1x10-2 s-1), while the rate sensitivities of both alloys were similar in the quasi-static-high strain rate range (1x10-4 and ∼2500-2800 s-1) at low strains. A more rapid decrease in the rate sensitivity of C-316L at increasing strains was found in the quasi-static-high strain rate range. The similar activation volumes of both alloys, corresponding to the dislocation intersections, indicated a similar thermally activated deformation process involvement in both alloys.
Appears in Collections:Mechanical Engineering / Makina Mühendisliği
Scopus İndeksli Yayınlar Koleksiyonu / Scopus Indexed Publications Collection
WoS İndeksli Yayınlar Koleksiyonu / WoS Indexed Publications Collection

Files in This Item:
File Description SizeFormat 
12174.pdfArticle14.66 MBAdobe PDFView/Open
Show full item record

CORE Recommender


checked on Mar 1, 2024


checked on Mar 2, 2024

Page view(s)

checked on Feb 26, 2024


checked on Feb 26, 2024

Google ScholarTM



Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.