Title: Structural, compositional and mechanical characterization of plasma nitrided CoCrMo alloy
Authors: Öztürk, Orhan
Okur, Serdal
Issue Date: 2009
Publisher: Izmir Institute of Technology
Abstract: Plasma nitriding techniques can be used to create wear and corrosion protective layers on the surface of CoCrMo alloys by modifying the near surface layers of these materials. In the present study, a medical grade CoCrMo alloy was nitrided in a low-pressure ( 60 mTorr) R. F. plasma at 400 Cfor 1, 2, 4, 6, and 20 hours under a gas mixture of 60% N2 . 40% H2. The structural as well as compositional characterization of the plasma nitrided layers were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM), and glow discharge optical emission spectroscopy (GDOES). The hardness and wear behaviour of the nitrided layers were performed by a microhardness tester and a pin-on-disk wear apparatus. The experimental analyses indicate that the expanded austenite phase, YN, with high N contents ( 30 at.%) is formed by the plasma nitriding process at 400 C. However, at longer nitriding times (6 and 20 h) there is decomposition into CrN in the YN matrix and a preferential (200) orientation of YN grains parallel to the surface develops. Based on the microscopy analyses of the electrochemically and Ar ion beam etched nitrided sample cross-sections and on the GDOES data, the YN layer thicknessesare found to be ranging from 2 to 10 microns. Based on the thickness data, an average N diffusion coefficient for the CoCrMo samples plasma nitrided at 400 C is estimated to be near 2x10-11 cm2/s. While significant improvements in hardness and wear volume reductions are observed for all the plasma nitrided alloys compared to the untreated alloy, the CoCrMo alloys with the YN structure only had the best combined wear-corrosion protection.
Description: Thesis (Master)--Izmir Institute of Technology, Physics, Izmir, 2009
Includes bibliographical references (leaves: 103-107)
Text in English; Abstract: Turkish and English
xv, 107 leaves
URI: http://hdl.handle.net/11147/3036
Appears in Collections:Master Degree / Yüksek Lisans Tezleri

Files in This Item:
File Description SizeFormat 
T000079.pdfMasterThesis4.22 MBAdobe PDFThumbnail
View/Open
Show full item record


CORE Recommender

Page view(s)

102
checked on Mar 20, 2023

Download(s)

120
checked on Mar 20, 2023

Google ScholarTM

Check





Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.