Title: Inertial effect in aluminum metal foams
Authors: Güden, Mustafa
Kocatürk, Onur
Issue Date: 2011
Publisher: Izmir Institute of Technology
Abstract: In this study, Al tubes, Al foams of different types, Al sandwich plates of various configurations (orientations) and brittle glass foam samples were quasistatically reloaded in order to assess any micro inertia effect on the deformation stresses. Al foams tested quasi-statically were further reloaded (interrupted test) in Split Hopkinson Bar (SHPB) at dynamic strain rates in order to see effect of strain rate on micro inertia effect. Al empty tubes experienced micro inertia independent (Type I) deformation behavior in lateral compression and micro inertia dependent (Type II) deformation behavior in axial compression. The lack of strain rate sensitivity of the tested Alulight (AlSi10) closed cell Al foams (Al/Si) produced through powder route within the studied strain rate regime was attributed to the foam cell wall fracture during cell wall buckling. While Al foams with and without SiC addition showed micro inertia effect through progressive cell wall bending. In accord with these observations, Al and Al/SiC foams showed the strain rate sensitive, while Alulight foams showed strain rate insensitive plateau stress in the SHPB compression tests. The layer configuration/orientation was shown to affect Al sandwich plate deformation. Progressive bending of the interlayer fins resulted in strain rate depending crushing stress, while shearing of the interlayer resulted in strain rate insensitive deformation stress. As was expected, the strength enhancement was not seen in glass foam specimens tested as the cell walls were fractured under compressive loads. Finally, a simple testing method was shown to investigate micro inertia effect in hollow and cellular Al structures.
Description: Thesis (Master)--Izmir Institute of Technology, Mechanical Engineering, Izmir, 2011
Includes bibliographical references (leaves: 68-71)
Text in English; Abstract: Turkish and English
xi, 71 leaves
Appears in Collections:Master Degree / Yüksek Lisans Tezleri

Files in This Item:
File Description SizeFormat 
T000989.pdfMasterThesis6.54 MBAdobe PDFThumbnail
Show full item record

CORE Recommender

Page view(s)

checked on Jun 19, 2023


checked on Jun 19, 2023

Google ScholarTM


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.