Title: Preparation and characterization of chitosan/calcium phosphate based composite biomaterials
Authors: Yıldırım, Oktay
Advisors: Çiftçioğlu, Muhsin
Publisher: Izmir Institute of Technology
Abstract: In this study the preparation and characterization of three-dimensional chitosan-calcium phosphate composite structures and porous hydroxyapatite bodies for biomaterial applications have been studied. The effects of chitosan calcium phosphate amount on density, porosity, microstructure, chemical composition and mechanical properties on the composites and effects of porosifier contents, hydroxyapatite content of the slurry and sintering temperature on density, porosity and microstructure of the porous ceramic samples were investigated. SEM was used for microstructural analysis, XRD and FTIR were used for chemical analysis, Archimedes method was used for investigating physical properties and compression test for investigating mechanical properties. In this study low molecular weight chitosan, -tricalciumphosphate, hydroxyapatite and hydroxyapatite whisker have been used. For composites freeze drying technique and for the porous bodies dry pressing, polymer sponge method and dough method have been used.The densities of the composites prepared by using chitosan as the matrix and hydroxyapatite, hydroxyapatite whisker, and B-tricalciumphosphate as reinforcement increased and the porosities decreased with the increase in the ceramic content. The modulus of elasticity and the yield stress generally increased with the increasing ceramic content except for the chitosan/-tricalciumphosphate composites. The densities and porosities of the composite structures varied in the range of 0.059-0.29 g/cm3 and 96-88% respectively. The elastic moduli of the composites varied in a range of 4.45-10.09 MPa and yield stress varied in a range of 0.14-0.34 Mpa due to the change in the ceramic weight%. Changing the ceramic weight% also had influence on the microstructure. Generally with increasing ceramic content the pore sizes decreased.The pore sizes varied in a range between 100-250, 100-400 and 100-200 for chitosan/hydroxapatite, Chitosan/-TCP/Hydroxyapatite and chitosan/HA whisker composites respectively. FTIR and XRD analysis showed that the composite structures contained original constituents, no new chemical compounds were formed the production process had not affected crystallinity of ceramic phases. The densities of the porous ceramic bodies decreased and the porosities increased with the increasing porosifier content at the porous ceramics prepared by dough method and dry pressing method. The porosity and density values of porous hydroxyapatite samples changed in range of 34-72% and 2.03 to 0.87 g/cm3. Pore sizes of polymeric sponge samples were found to be around 300-400 and dry pressing and dough method samples were found to be 10u.
Description: Thesis (Master)--Izmir Institute of Technology, Materials Science and Engineering, Izmir, 2004
Includes bibliographical references (leaves: 94)
Text in English; Abstract: Turkish and English
xvi, 97 leaves
URI: http://hdl.handle.net/11147/3299
Appears in Collections:Master Degree / Yüksek Lisans Tezleri

Files in This Item:
File Description SizeFormat 
T000452.pdfMasterThesis5.73 MBAdobe PDFThumbnail
View/Open
Show full item record



CORE Recommender

Page view(s)

194
checked on Mar 25, 2024

Download(s)

160
checked on Mar 25, 2024

Google ScholarTM

Check





Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.