Title: Structural investigation and wettability of PVD TiN caoted CoCrMo orthopedic alloy
Authors: Çağlar, Özlem
Advisors: Öztürk, Orhan
Publisher: 01. Izmir Institute of Technology
Abstract: Wettability, defined as the ability of any solid surface to be wetted when in contact with a liquid, is one of the most important properties of biomaterials since highly wettable surfaces are expected to disclose better adhesion of the cells.The wettability characteristics of a biomaterial.s surface can be improved by surface modification techniques.In this study, wettability characteristics of TiN coated CoCrMo orthopedic alloy materials were investigated. CoCrMo alloys were coated with TiN using physical vapor deposition (PVD) technique at 550 C for 6 h. The TiN coated layer microstructure,roughness, thickness, and composition were studied by X-ray diffraction (XRD), atomic force microscopy (AFM) and scanning electron microscope (SEM). Wetting studies involved contact angle and surface tension measurements using distilled water and simulated body fluid (SBF) as test liquids. The contact angles of the coated and uncoated CoCrMo alloys were investigated by the sessile drop method and the surface tension of the test liquids was measured by the ring method. The XRD results show the PVD coated TiN films had (111) preferred orientation, while the SEM analysis indicated quite uniform TiN coated layers (about 3 m thick) with a columnar growth mode. The AFM results indicated much higher roughness values for the TiN coated surfaces compared to the uncoated ones. The experimental results show the contact angle values for the TiN coated samples is lower than the uncoated ones suggesting better wetting for the coated layer. Based on the contact angle and the surface tension values, the work of adhesion values were estimated and it was found that the TiN coated layers has better adhesion ability compared to the uncoated CoCrMo alloy. The lower contact angles for the TiN coated samples were attributed mainly to the rougher surfaces associated with the TiN coated surfaces in comparison with the relatively smooth surface of the uncoated samples. Also, based on the EDX analysis results, the surface oxygen content on the coated surface may be another factor contributing to the better wettability characteristics of the TiN coated CoCrMo alloy compared to the uncoated alloy.
Description: Thesis (Master)--İzmir Institute of Technology, Physics, İzmir, 2007
Includes bibliographical references (leaves: 58-62)
Text in English; Abstract: Turkish and English
x, 62 leaves
URI: http://hdl.handle.net/11147/3364
Appears in Collections:Master Degree / Yüksek Lisans Tezleri

Files in This Item:
File Description SizeFormat 
T000663.pdfMasterThesis4.03 MBAdobe PDFThumbnail
View/Open
Show full item record



CORE Recommender

Page view(s)

90
checked on Mar 25, 2024

Download(s)

212
checked on Mar 25, 2024

Google ScholarTM

Check





Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.