Title: Designing and processing of porous Ti6A14V cages for spinal surgery
Authors: Güden, Mustafa
Hızal, Alpay
Issue Date: 2007
Publisher: Izmir Institute of Technology
Abstract: Ti6Al6V foam materials were prepared with spherical particles in range of 20 90mm. Average porosity under various compaction pressure (200 MPa, 400 MPa, 500MPa, 600MPa, 700MPa), sintering temperature (1000oC-1400oC) and time (4h-6h) was observed in the range of 52%-72%. It was observed that sintered Ti6Al4V foam material can be potentially used for the spinal surgery. Furthermore, strength of the Ti6Al4V foam material in the porosity level of 40% is comparable with the human cortical bone. And also 22 Design of Experiment methods were used to investigate the major affective parameters during the processing of Ti6Al4V spinal cages. According to this investigation, sintering temperature, particle diameter and compaction pressure are the most affective parameters control the over all process of foam production. In the design process, protection case also designed for the foam material to put them inside of it. The reason of producing protection case is that eliminating the particle loosing from the sharp edges of the Ti6Al4V foam material.
Description: Thesis (Master)--Izmir Institute of Technology, Mechanical Engineering, Izmir, 2007
Includes bibliographical references (leaves: 81-84)
Text in English; abstract: Turkish and English
xii, 150 leaves
Appears in Collections:Master Degree / Yüksek Lisans Tezleri

Files in This Item:
File Description SizeFormat 
T000620.pdfMasterThesis19.74 MBAdobe PDFThumbnail
Show full item record

CORE Recommender

Page view(s)

checked on Feb 23, 2024


checked on Feb 23, 2024

Google ScholarTM


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.