Title: Investigation of magnetic dead layer formation at the interfaces of sputtered Ni80 Fe20 thin films
Authors: Tarı, Süleyman
Alagöz, Hüseyin Serhat
Issue Date: 2009
Publisher: Izmir Institute of Technology
Abstract: In this thesis, magnetic dead layer formation at the interfaces of the sputtered Ni80Fe20 thin films has been investigated experimentally. Different insulators such as Ta2O5, Al2O3 and metallic Ta thin films have been deposited as seed and cap layers to determine the MDL formation at the interface of Ni80Fe20. The magnetization of samples has been probed by Vibrating sample magnetometry and X-ray reflectivity measurements have been carried out to investigate the thickness and roughness of the interlayers. Ta films cause the most MDL formation when grown as seed as well as cap layer. It has been observed that the thickness of MDL is strongly temperature dependent. MDL thickness decreases for all trilayers deposited except for Ta2O5/Ni80Fe20/Ta2O5 when they are exposed to 300 .C annealing temperature. Further annealing at 500 .C causes an interdiffusion between the layers and the thickness of the MDL increases. According to XRR measurements, the thickness of the inter alloy layers between the Ni80Fe20 and its adjacent layers is consistent with the thickness of magnetic dead layer calculated from Liebermann equation. MDL calculations reveal that SiO2/Ta/Ni80Fe20/Al2O3 multilayer has the lowest MDL thickness therefore might be a possible candidate to be used in spin valve structures.
Description: Thesis (Master)--Izmir Institute of Technology, Physics, Izmir, 2009
Includes bibliographical references (leaves: 57-60)
Text in English; Abstract:Turkish and English
xi, 60 leaves
URI: http://hdl.handle.net/11147/3979
Appears in Collections:Master Degree / Yüksek Lisans Tezleri

Files in This Item:
File Description SizeFormat 
T000807.pdfMasterThesis1.84 MBAdobe PDFThumbnail
View/Open
Show full item record



CORE Recommender

Page view(s)

70
checked on Feb 19, 2024

Download(s)

50
checked on Feb 19, 2024

Google ScholarTM

Check





Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.