Title: Grawth and electrical characterization of high purity carbon nanotubes
Authors: Selamet, Yusuf
Kır, Serap
Issue Date: 2009
Publisher: Izmir Institute of Technology
Abstract: This thesis work is focused on growing high purity vertically aligned Carbon nanotubes by ethylene gas thermal chemical vapor deposition method on very thin Cobalt and Iron catalyst thin films deposited on to Si/SiO2/Al2O3 substrates by DC magnetron sputtering. In this study, the effective parameters were changed to grow aligned CNTs. Hence, the vertically aligned CNTs were performed and also the ideal parameters were determined for this kind of growth mechanism. The effect of support layer was examined for three different hydrocarbon gas ratios. SiO2 and Al2O3 were used as support layers between metal catalyst thin films and Si substrate. Two kinds of samples were compared; one of them had only Al2O3 and the other one includes both Al2O3 and SiO2 layers. As a result, the sample that had both oxide layers gave better results for density of CNTs on the surface of samples. Moreover, types of catalyst material effect also were examined on growth of CNTs for three different temperatures. For this aim, the performance of Fe and Co catalyst thin films was compared. According to our results, Fe was more reactive with ethylene gas than Co catalysts and also, the density of CNTs was increased by using Fe as a catalyst material. Hydrogen pretreatment time was performed for another significant effect. Seven different time parameter which were 0, 5, 10, 15, 20, 25, 30 minutes, were examined. The density and diameters of catalysts particles were compared for these different treatment times. Finally, the electrical characterization of CNTs was performed. The resistance of CNTs was measured by using two point contact technique. Moreover, the interaction between resistance of CNTs and humidity was examined.
Description: Thesis (Master)--Izmir Institute of Technology, Physics, Izmir, 2009
Includes bibliographical references (leaves: 56-66)
Text in English; Abstract:Turkish and English
xi, 66 leaves
Appears in Collections:Master Degree / Yüksek Lisans Tezleri

Files in This Item:
File Description SizeFormat 
T000213.pdfMasterThesis9.74 MBAdobe PDFThumbnail
Show full item record

CORE Recommender

Page view(s)

checked on Feb 26, 2024


checked on Feb 26, 2024

Google ScholarTM


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.