Title: Growth and structural characterization of Fe/TaOx/Fe magnetic multilayers
Authors: Tari, Süleyman
Oğuz, Kaan
Issue Date: 2006
Publisher: Izmir Institute of Technology
Abstract: In this thesis, we are proposing to fabricate and structurally characterize Fe/TaOx/Fe magnetic multilayers as an initiative work towards magnetic tunnel junction (MTJ) structures with TaOx spacer layer. The multilayer structures were grown by magnetron sputtering technique and characterized by X-Ray Diffraction (XRD), Atomic Force Microscopy (AFM), and Scanning Electron Microscopy (SEM). Ellipsometry was used to find the refractive index and the hysteresis loops were taken by SQUID Magnetometer. It was found that Fe grew 45 degree tilted epitaxial single crystal on Si (001) substrate at room temperature. Ta growth on silicon had poor crystal quality due to large lattice mismatch between tantalum and silicon however Ta single layer on Fe was found to be single crystal with 0.72 FWHM. Reactive oxidation of Ta film resulted in formation of amorphous Ta2O5 with refractive index of 2.1. Fe, Ta, and TaOx single layer films were found to be uniform and smooth on silicon substrate. Bilayer of Fe/Ta and Fe/TaOx were also investigated to understand the behavior of single layer films on top of each other. Multilayers with Ta and TaOx spacer layers were successfully grown and these multilayers showed good structural properties. Furthermore, hysteresis loops of Fe films as thin as 50 nm showed magnetization comparable with the bulk Fe with the coercive field of 20 Oe.
Description: Thesis (Master)--Izmir Institute of Technology, Physics, Izmir, 2006
Includes bibliographical references (leaves: 57-61)
Text in English; Abstract:Turkish and English
x, 61 leaves
Appears in Collections:Master Degree / Yüksek Lisans Tezleri

Files in This Item:
File Description SizeFormat 
T000529.pdfMasterThesis2.62 MBAdobe PDFThumbnail
Show full item record

CORE Recommender

Page view(s)

checked on Nov 27, 2023


checked on Nov 27, 2023

Google ScholarTM


Items in GCRIS Repository are protected by copyright, with all rights reserved, unless otherwise indicated.